Hardness greater than 1200 HV zirconia ceramic blocks designed for Amann Girrbach system ensuring durability and precision

Product Description:

This innovative multilayer zirconia material is engineered to gradually transition in its properties, including strength, color, translucency, and hardness, moving from the cervical area to the incisal edge. This gradient design ensures a more natural and lifelike appearance.

As the world’s first zirconia product featuring 8 distinct layers and 15 different gradients, it offers exceptional aesthetic results while maintaining superior durability. This unique combination makes it ideal for a variety of dental restorations.

It is suitable for use in anterior crowns, posterior crowns, as well as bridges up to 14 units in length. The material exhibits impressive characteristics such as a flexural strength ranging between 700 and 1200 MPa and requires a sintering temperature of 1500°C.

Translucency values vary from 43% to 57%, contributing to its natural look, and it is available in 16 Vita shades along with 3 additional bleach shades, providing a wide range of options to match individual patient needs.

Features:

• Product Name: Multilayer Zirconia Block
• Contains 8 layers for enhanced esthetics and strength
• High bending strength of 900 MPa for durable dental restorations
• Density ranges between 6.0-6.3 g/cm³ ensuring reliable material quality
• Sintering program at 1500 degrees for optimal material properties
• 100% precise scaling factor for accurate fit and milling
• Ideal choice as a dental zirconia block for various dental applications
• Multilayer zirconia disc design provides natural gradient shading

Applications:

The Wecera Super 8 3D multilayer zirconia is an advanced dental zirconia block designed to meet the highest standards of dental restoration. Originating from China and certified by CE, FDA, and ISO13485, this multilayer zirconia disc is ideal for dental laboratories and clinics seeking reliable and high-performance materials. Its compatibility with the Amann Girrbach System ensures seamless integration into existing workflows, enabling precise and efficient fabrication of dental prosthetics.

Thanks to its impressive sintering density of 6.0g/cm³ and overall density ranging between 6.0-6.3g/cm³, the Wecera Super 8 zirconia block offers exceptional stability and durability. With a bending strength of 900 MPa, it provides outstanding mechanical properties, making it suitable for producing crowns, bridges, inlays, onlays, and implant abutments that require long-lasting strength and resistance. The low chemical solubility of less than 100 μg/cm² further enhances its suitability for intraoral applications by ensuring minimal degradation over time.

This multilayer zirconia disc is especially advantageous in scenarios where aesthetic appeal and functional performance must be balanced. Its multilayer structure mimics the natural gradient of tooth coloration, allowing dental professionals to create restorations that blend seamlessly with the patient’s existing teeth. This makes it an excellent choice for anterior and posterior restorations, where both durability and appearance are critical. Furthermore, the 3D multilayer zirconia technology facilitates easier milling and sintering processes, reducing production time and improving overall efficiency in dental labs.

The Wecera Super 8 multilayer zirconia block is perfect for use in dental clinics and laboratories focused on CAD/CAM dentistry. It supports the fabrication of custom dental restorations with superior fit, strength, and aesthetics, ensuring patient satisfaction. Whether producing single-unit crowns or complex multi-unit bridges, this dental zirconia block delivers consistent, high-quality results. In summary, the Wecera Super 8 3d multilayer zirconia is an optimal solution for dental professionals seeking a certified, high-strength, and visually appealing material for modern dental restoration applications.

Customization:

Wecera offers customizable product services for the Super 8 multilayer zirconia block, a premium 3d multilayer zirconia solution designed for advanced dental restorations. Manufactured in China, this multilayer zirconia disc features pre-shaded zirconia blocks available in a range of colors from A1 to D4, ensuring optimal aesthetic results for various dental applications.

The Super 8 model boasts a high bending strength of 900Mpa and a density between 6.0-6.3g/cm3, providing exceptional durability and reliability in zirconia dental ceramics. With a diameter of 98mm, these discs are suitable for various milling machines and workflows.

Certified by CE, FDA, and ISO13485, Wecera’s multilayer zirconia disc meets stringent quality and safety standards. Our product customization services allow dental laboratories and clinics to tailor specifications according to their unique needs, ensuring precise fit and superior performance in dental restorations.

Support and Services:

Our Multilayer Zirconia Block is designed to provide exceptional strength, durability, and aesthetic appeal for dental restorations. To ensure optimal performance and longevity of the product, please follow the recommended guidelines and support services outlined below.

Technical Support:

Our technical support team is dedicated to assisting you with any questions or issues related to the Multilayer Zirconia Block. We provide comprehensive guidance on product selection, handling, milling parameters, sintering protocols, and finishing techniques to help you achieve the best results.

Product Handling:

Handle the zirconia blocks with care to prevent contamination or damage. Store the blocks in a dry, temperature-controlled environment away from direct sunlight. Avoid exposure to moisture or extreme temperatures before processing.

Milling Instructions:

Use compatible CAD/CAM milling machines and follow the manufacturer's recommended settings for cutting speed, feed rate, and tool selection. Ensure that milling tools are sharp and in good condition to prevent chipping or cracking of the zirconia.

Sintering Guidelines:

Adhere strictly to the sintering schedule provided with the product. Use a calibrated sintering furnace and ensure proper temperature ramp-up and cooling rates to achieve optimal density and mechanical properties. Avoid rapid cooling to prevent internal stresses.

Finishing and Polishing:

After sintering, finish and polish the restorations using recommended diamond burs and polishing kits. Proper finishing enhances the aesthetic quality and reduces wear on opposing dentition.

Warranty and Service:

The Multilayer Zirconia Block is backed by a quality assurance warranty covering manufacturing defects. For any product-related concerns, technical questions, or service requests, please consult our support resources to facilitate prompt assistance.

Training and Resources:

We offer training sessions and detailed instructional materials to help dental technicians and clinicians maximize the benefits of the Multilayer Zirconia Block. Access to webinars, user manuals, and troubleshooting guides is available to support your practice.

By following these technical support and service recommendations, you can ensure the highest quality outcomes and patient satisfaction with the Multilayer Zirconia Block dental restorations.